Thermal barrier coating systems and processes therefor

ABSTRACT

Coating systems and processes by which the coating systems can be deposited to be resistant to contaminants, and particularly resistant to infiltration and damage caused by CMAS. The coating systems include inner and outer ceramic layers, each having a microstructure characterized by splats and horizontal porosity. The inner ceramic layer consists essentially of zirconia stabilized by about 6 to about 9 weight percent yttria. The outer ceramic layer overlies and contacts the inner ceramic layer to define the outermost surface of the coating system. The outer ceramic layer consists essentially of zirconia stabilized by about 25 to about 75 weight percent yttria, has a thickness that is less than the thickness of the inner ceramic layer, and has a porosity level that is lower than that of the inner ceramic layer.

CROSS REFERENCE TO RELATED APPLICATIONS

This is a division patent application of co-pending U.S. patentapplication Ser. No. 13/341,247, filed Dec. 30, 2011, which claimed thebenefit of U.S. Provisional Application No. 61/546,793, filed Oct. 13,2011. The contents of these prior applications are incorporated hereinby reference.

BACKGROUND OF THE INVENTION

This invention relates to coatings capable of use on components exposedto high temperatures, such as the hostile thermal environment of a gasturbine engine. More particularly, this invention is directed to athermal barrier coating (TBC) capable of exhibiting resistance tothermal cycling and infiltration by contaminants, for example, of typesthat may be present in the operating environment of a gas turbineengine.

The use of thermal barrier coatings (TBCs) on components such ascombustors, high pressure turbine (HPT) blades, vanes and shrouds isincreasing in commercial as well as military gas turbine engines. Thethermal insulation provided by a TBC enables such components to survivehigher operating temperatures, increases component durability, andimproves engine reliability. TBCs are typically formed of a ceramicmaterial and deposited on an environmentally-protective bond coat toform what is termed a TBC system. Bond coat materials widely used in TBCsystems include oxidation-resistant overlay coatings such as MCrAlX(where M is iron, cobalt and/or nickel, and X is yttrium or another rareearth element), and diffusion coatings such as diffusion aluminides thatcontain aluminum intermetallics. Bond coat materials are typicallyselected to be capable of forming a continuous and adherent oxide scaleon their surface to promote the adhesion of the ceramic coating to thebond coat. The oxide scale can be formed by subjecting the bond coat toan oxidizing environment, such that the scale is sometimes referred toas a thermally-grown oxide (TGO).

Notable examples of ceramic materials for TBCs include zirconiapartially or fully stabilized with yttria (yttrium oxide; Y₂O₃) oranother oxide, such as magnesia, ceria, scandia and/or calcia, andoptionally other oxides to reduce thermal conductivity. Binaryyttria-stabilized zirconia (YSZ) is widely used as a TBC materialbecause of its high temperature capability, low thermal conductivity,and relative ease of deposition. Zirconia is stabilized to inhibit atetragonal to monoclinic crystal phase transformation at about 1000° C.,which results in a volume change that can cause spallation. At roomtemperature, the more stable tetragonal phase is obtained and themonoclinic phase is minimized if zirconia is stabilized by at leastabout six weight percent yttria. A stabilizer (e.g., yttria) content ofseventeen weight percent or more ensures a fully stable cubic crystalphase. The conventional practice has been to partially stabilizezirconia with six to eight weight percent yttria (6-8% YSZ) to obtain aTBC that is adherent and spallation-resistant when subjected to hightemperature thermal cycling. Furthermore, partially stabilized YSZ(e.g., 6-8% YSZ) is known to be more erosion-resistant than fullystabilized YSZ (e.g., 20% YSZ).

Various process can be used to deposit TBC materials, including thermalspray processes such as air plasma spraying (APS), vacuum plasmaspraying (VPS), low pressure plasma spraying (LPPS), and high velocityoxy-fuel (HVOF). TBCs employed in the highest temperature regions of gasturbine engines are often deposited by a physical vapor deposition(PVD), and particularly electron beam physical vapor deposition (EBPVD),which yields a columnar, strain-tolerant grain structure that is able toexpand and contract without causing damaging stresses that lead tospallation. Similar columnar microstructures can be produced using otheratomic and molecular vapor processes, such as sputtering (e.g., high andlow pressure, standard or collimated plume), ion plasma/cathodic arcdeposition, and all forms of melting and evaporation depositionprocesses (e.g., laser melting, etc.). TBCs formed by the variousmethods noted above generally have a lower thermal conductivity than adense ceramic of the same composition as a result of the presence ofmicrostructural defects and pores at and between grain boundaries of theTBC microstructure.

Under service conditions, hot section engine components protected by aTBC system can be susceptible to various modes of damage, includingerosion, oxidation and corrosion from exposure to the gaseous productsof combustion, foreign object damage (FOD), and attack fromenvironmental contaminants. The source of environmental contaminants isambient air, which is drawn in by the engine for cooling and combustion.The type of environmental contaminants in ambient air will vary fromlocation to location, but can be of a concern to aircraft as theirpurpose is to move from location to location. Environmental contaminantsthat can be present in the air include sand, dirt, volcanic ash, sulfurin the form of sulfur dioxide, fly ash, particles of cement, runwaydust, and other pollutants that may be expelled into the atmosphere,such as metallic particulates, for example, magnesium, calcium,aluminum, silicon, chromium, nickel, iron, barium, titanium, alkalimetals and compounds thereof, including oxides, carbonates, phosphates,salts and mixtures thereof. These environmental contaminants are inaddition to the corrosive and oxidative contaminants that result fromthe combustion of fuel. However, all of these contaminants can adhere tothe surfaces of the hot section components, including those that areprotected with a TBC system.

In order for a TBC to remain effective throughout the planned life cycleof the component it protects, it is important that the TBC has andmaintains integrity throughout the life of the component, including whenexposed to contaminants. Some contaminants may result in TBC loss overthe life of the components. For example, particulates of calcia (CaO),magnesia (MgO), alumina (aluminum oxide; Al₂O₃) and silica (silicondioxide; SiO₂) are often present in environments containing fine sandand/or dust. When present together at elevated temperatures, calcia,magnesia, alumina and silica can form a eutectic compound referred toherein as CMAS. A particular composition that has been identified forCMAS contains about 35 mol % CaO, about 10 mol % MgO, about 7 mol %Al₂O₃, and about 48 mol % SiO₂, along with about 3 mol % Fe₂O₃ and about1.5 mol % NiO. CMAS has a relatively low melting temperature, such thatduring turbine operation the CMAS that deposits on a component surfacecan melt, particularly if surface temperatures exceed about 2240° F.(1227° C.). Molten CMAS is capable of infiltrating the porosity withinTBCs. For example, CMAS is capable of infiltrating into TBCs havingcolumnar structures, dense vertically-cracked TBCs, and the horizontalsplat boundaries of TBCs deposited by thermal and plasma spraying. Themolten CMAS resolidifies within cooler subsurface regions of the TBC,where it interferes with the compliance of the TBC and can lead tospallation and degradation of the TBC, particularly during thermalcycling as a result of interfering with the ability of the TBC to expandand contract. In addition to loss of compliance, deleterious chemicalreactions with yttria and zirconia within the TBC, as well as with thethermally-grown oxide at the bond coating/TBC interface, can occur andcause degradation of the TBC system. Once the passive thermal barrierprotection provided by the TBC has been lost, continued operation of theengine will lead to oxidation of the base metal beneath the TBC system,which may ultimate lead to failure of the component by burn throughcracking

Attempts to mitigate the effect of the CMAS on high pressure turbineblades have included the application of a thin layer of alumina on thesurface of the TBC to increase the melting point of CMAS by about 100 to150° F. (38° C. to 66° C.). The addition of the alumina layer providesan increase in operating temperature of up to about 2400° F. (1316° C.)with reduced infiltration of liquid CMAS. However, grinding duringmanufacture and assembly, as well as grinding and rubbing with turbineshrouds during gas turbine engine operation, result in the use andreliance on the alumina layer difficult and impractical. In addition,the alumina layer adds manufacturing cost and complexity, especially forturbine blades that are subjected to gas and particle erosion and mayhave different requirements for the alumina coating in order to minimizeerosion. In addition, thicker alumina layers are subject to coefficientof thermal expansion mismatches within the TBC coating system, resultingin thermal strains during cycling.

In view of the above, it can be appreciated that there are certainproblems, shortcomings or disadvantages associated with the prior art,and that it would be desirable if systems and methods were availablethat are capable of promoting the resistance of components tocontaminants, such as CMAS, and particularly gas turbine enginecomponents that operate at temperatures above the melting temperaturesof contaminants.

BRIEF DESCRIPTION OF THE INVENTION

The present invention provides a coating system and a process by whichthe coating system can be deposited to be resistant to contaminants, andparticularly resistant to infiltration and damage caused by CMAS.

According to a first aspect of the invention, a coating system isprovided on a surface region of a component. The coating system includesa bond coat and inner and outer ceramic layers overlying the bond coat.Each of the inner and outer ceramic layers has a microstructurecharacterized by splats and horizontal porosity. The inner ceramic layeroverlies the bond coat, consists essentially of zirconia stabilized byabout 6 to about 9 weight percent yttria, and has a thickness andporosity level. The outer ceramic layer overlies and contacts the innerceramic layer to define the outermost surface of the coating system. Theouter ceramic layer consists essentially of zirconia stabilized by about25 to about 75 weight percent yttria, has a thickness that is less thanthe thickness of the inner ceramic layer, and has a porosity level thatis lower than the inner ceramic layer.

According to a second aspect of the invention, a process is provided forforming a coating system on a component. The process includes depositinga bond coat on a surface of the component, depositing an inner ceramiclayer on the bond coat, and then depositing an outer ceramic layer onthe inner ceramic layer to define an outermost surface of the coatingsystem. The inner and outer ceramic layers are deposited using a thermalspray process to yield a microstructure characterized by splats andhorizontal porosity. The inner ceramic layer consists essentially ofzirconia stabilized by about 6 to about 9 weight percent yttria and isdeposited to have a thickness and a porosity level. The outer ceramiclayer consists essentially of zirconia stabilized by about 25 to about75 weight percent yttria, and is deposited to have a thickness that isless than the thickness of the inner ceramic layer and a porosity levelthat is lower than the inner ceramic layer. The inner and outer ceramiclayers are then heat treated to a temperature and for a durationsufficient to relieve stresses therein induced by the depositing steps.

A technical effect of the invention is the ability of the coating systemto withstand thermal cycling when subjected to CMAS contaminants. Thehigh yttria content of the outer ceramic layer enables the outer ceramiclayer to react with CMAS to form a protective layer that inhibitsfurther infiltration of molten CMAS into the coating system.Significantly, the relative thicknesses and densities of the inner andouter ceramic layers have been shown to be critical to the spallationresistance of the coating system. In particular, the spallationresistance of the coating system has been shown to be significantlyenhanced by limiting the thickness of the outer ceramic layer relativeto the thickness of the inner ceramic layer and by ensuring that theouter ceramic layer is denser (less porous) than the inner ceramiclayer.

Other aspects and advantages of this invention will be betterappreciated from the following detailed description.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 schematically represents a cross-section through a TBC system.

FIG. 2 is a phase diagram for the zirconia-yttria system.

FIG. 3 is a scanned images of a TBC system in accordance with anembodiment of this invention.

FIG. 4 is a graph comparing the relative resistance of TBC systemswithin and outside the scope of the invention when subjected to thermalcycling.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is generally applicable to components subjected tohigh temperatures, and particularly to components such as the high andlow pressure turbine vanes (nozzles) and blades (buckets), shrouds,combustor liners and augmentor hardware of gas turbine engines. Theinvention provides TBC systems that are suitable for protecting thesurfaces of gas turbine engine components that are subjected to hotcombustion gases. While the advantages of this invention will bedescribed with reference to gas turbine engine components, the teachingsof the invention are generally applicable to any component on which aTBC may be used to protect the component from a high temperatureenvironment.

An embodiment of a TBC system 10 of this invention is schematicallyrepresented in FIG. 1 as being applied to the surface of a substrate 22,which in combination with the TBC system 10 yields a coated component20. The TBC system 10 is shown as including a bond coat 12 that overliesthe surface of a substrate 22, the latter of which may be a superalloyor another high temperature material. The substrate 22 is typically thebase material of the component 20 protected by the TBC system 10, thoughthe substrate 22 may instead be a coating on the component. The bondcoat 12 may be an aluminum-rich composition of a type typically usedwith TBC systems for gas turbine engine components, such as an overlaycoating of an MCrAlX alloy or a diffusion coating such as a diffusionaluminide (including diffusion aluminide coatings modified by a preciousmetal, for example, platinum) of a type known in the art. A particularexample is a NiCrAlY composition of a type known in the art. A suitablethickness for the bond coat 12 is about 0.007 inch (about 175micrometers), though lesser and greater thicknesses are foreseeable aslong as the bond coat 12 is capable of providing the desired functionsof protecting the substrate 22 and anchoring the TBC system 10.Aluminum-rich bond coats of the types noted above develop an aluminumoxide (alumina) scale (not shown), which is thermally grown by oxidationof the bond coat 12.

Also shown in FIG. 1 is a multilayer TBC 14 overlying the bond coat 12.The TBC 14 comprises an inner TBC layer 16 that has been depositeddirectly on the bond coat 12 so as to overlie the bond coat 12, and anouter TBC layer 18 that has been deposited directly on the inner TBClayer 16 so as to overlie the inner TBC layer 16 and define theoutermost surface 24 of the TBC system 10 and component 20. As such, ifthe component 20 is subjected to contaminants, the contaminants would bedeposited directly onto the surface 24 of the outer TBC layer 18.

According to a preferred aspect of the invention, the inner and outerTBC layers 16 and 18 are formed of YSZ materials having different yttriacontents. The yttria content of the outer TBC layer 18 of the TBC 14 ishigher than the yttria content on the inner TBC layer 16, and issufficiently high to promote the ability of the outer TBC layer 18 toreact with contaminants that may deposit on the outermost surface 24 ofthe TBC system 10. A contaminant of particular concern is theaforementioned CMAS, in which case the yttria content of the outer TBClayer 18 is able to react with molten CMAS deposits at temperaturesabove about 1200° C. (about 2200° F.) to form a protective reactionproduct that contains calcium yttrium silicate, which is often known asan apatite phase. The reaction product forms a dense adherent sealinglayer that protects the underlying TBC system 10 from furtherinfiltration of CMAS. Though the resistance to CMAS infiltration of aYSZ layer containing more than 20 weight percent yttria is taught inU.S. Pat. No. 7,862,901 to Darolia et al., TBC systems within the rangestaught by Darolia et al. were found to be prone to spallation. Thepresent invention is based on the determination that spallationresistance is achieved by more narrowly limiting the yttria content and,in particular, by controlling the relative thicknesses and densities ofthe inner and outer TBC layers 16 and 18, as discussed below.

According to preferred aspects of the invention, the outer TBC layer 18contains about 25 to about 75 wt. % yttria, with the balance beingessentially zirconia (allowing for incidental impurities). Morepreferably, the outer TBC layer 18 contains 30 to 59 wt. % andpreferably less than 55 wt. % yttria, with an yttria content of about 38wt % appearing to be particularly sufficient to enable the reaction thatforms the desired calcium yttrium silicate reaction product whileoffering greater erosion and spallation resistance than higher yttriacontents. In contrast, the inner TBC layer 16 has a lower yttriacontent, and can contain a generally conventional yttria content ofabout 6 to about 9 wt % yttria, with the balance being essentiallyzirconia (allowing for incidental impurities). As evident from FIG. 2,the phase diagram for the yttria-zirconia system shows the compositionof the inner TBC layer 16 as falling within the metastable tetragonal(or modified tetragonal) phase field, whereas the range of 30 to 59 wt.% yttria preferred for the outer TBC layer 18 lies entirely within thecubic phase field.

As noted above, the outer TBC layer 18 also differs from the inner TBClayer 16 in terms of its density (porosity) and thickness. Inparticular, the inner TBC layer 16 is deposited in a manner thatachieves a relatively porous macrostructure, preferably characterized bya porosity level of about 10 to about 25 volume percent, and morepreferably about 10 to about 20 volume percent. In contrast, the outerTBC layer 18 is deposited in a manner that achieves a less porousmacrostructure than the inner TBC layer 16. The outer TBC layer 18preferably has a porosity level of about 3 to about 15 volume percent,and more preferably about 5 to about 10 volume percent. The preferreddensity range and the relatively higher density of the outer TBC layer18 is necessary in view of the lower toughness and erosion resistance ofthe cubic YSZ phase within this layer 18 as compared to the tetragonalYSZ phase within the inner TBC layer 16.

To obtain the desire porosity levels in the TBC layers 16 and 18, theTBC layers 16 and 18 preferably have a noncolumnar structure as a resultof being deposited by a thermal spraying technique, for example, plasmaspraying (air (APS), vacuum (VPS) and low pressure (LPPS)) or highvelocity oxy-fuel (HVOF). As known in the art, thermal spraying involvespropelling melted or at least heat-softened particles of a heat fusiblematerial (e.g., metal, ceramic) against a surface, where the particlesare quenched and bond to the surface to produce a coating. As such, theinner and outer TBC layers 16 and 18 are deposited in the form of molten“splats,” resulting in a microstructure characterized by horizontalporosity resulting from the presence of the splats (flattened grains).The microstructures of either or both TBC layers 16 and 18 may bemodified to contain dense vertical cracks of the type taught in U.S.Pat. Nos. 5,073,433, 5,520,516, 5,830,586, 5,897,921, 5,989,343 and6,047,539.

The inner and outer TBC layers 16 and 18 and the bond coat 12 may bedeposited using the same thermal spray gun. Particular acceptableresults, including the desired difference in the densities of the TBClayers 16 and 18, have been obtained by controlling the surfacetemperatures and varying the standoff distances used to deposit the TBClayers 16 and 18. Particularly suitable results have been obtained bydepositing the bond coat 12 and inner TBC layer 16 using relativelyconventional plasma spray conditions including a standoff distance ofabout 4.5 to about 5 inches (about 11.4 to about 12.7 cm) and usingsweeping air while maintaining the surface temperature of the bond coat12 at about 75 to about 200° F. (about 24 to about 93° C.). In addition,particularly suitable results have been obtained by depositing the outerTBC layer 18 using a shorter standoff distance than used to deposit theinner TBC layer 16, for example, about 3 to about 3.25 inch (about 7.6to about 8.3 cm) using sweeping air while maintaining the depositionsurface of the inner TBC layer 16 at a higher temperature than used todeposit the inner TBC layer 16, for example, about 450 to about 550° F.(about 230 to about 260° C.). In other words, the outer TBC layer 18 maybe applied using the same thermal spray gun as used to deposit the innerTBC layer 16, but the TBC layer 18 is deposited on a hotter and closersubstrate surface than the TBC layer 16. The combined effect of theseparameters is to intentionally decrease the porosity of the outer TBClayer 18 relative to the inner TBC layer 16.

FIG. 3 shows a nonlimiting example of a TBC system containing a bondcoat and two TBC layers of the types described above. The bond coatappears as the lightest layer in the image, and the outer TBC layerappears as the darkest layer in the image.

Following the deposition of both TBC layers 16 and 18, the TBC system 10preferably undergoes heat treatment to relieve residual stresses. Anexemplary heat treatment is in a temperature range of about 1925 toabout 1975° F. (about 1050 to about 1080° C.) in a vacuum for a durationof about two to about four hours. A particularly preferred heattreatment is believed to be about 1975° F. (about 1080° C.) in a vacuumfor about four hours. This disclosed heat treatment is merely exemplaryand other effective heat treatments may be employed.

As noted above, the outer TBC layer 18 also differs from the inner TBClayer 16 in terms of its thickness. Investigations leading to thepresent invention evidenced that the relative thickness of the TBClayers 16 and 18 must be controlled in order to achieve improvements inspallation resistance of the TBC system 10, even in the absence of CMAScontaminants. In particular, testing indicated that the thickness ratioof the outer TBC layer 18 to the inner TBC layer 16 must be less thanone. FIG. 4 represents data accumulated from furnace cycle testingperformed under conditions that entailed one-hour cycles between roomtemperature and about 2075° F. (about 1135° C.), with a dwell time ofabout forty-five minutes at peak temperature. Testing of a specimen wasterminated when about 20% of the surface area of the TBC system hadspalled. Two sets of specimens were evaluated, each deposited onsubstrates formed of Rene N5 and provided with a bond coat formed ofNiCrAlY. A first set of the specimens had an inner TBC layer of about 7%YSZ that was about 3 mils thick (about 75 micrometers) and an outer TBClayer of about 38% YSZ that was about 12 mils thick (about 300micrometers). The second set of specimens had an inner TBC layer ofabout 7% YSZ that was about 10 mils thick (about 250 micrometers) and anouter TBC layer of about 38% YSZ that was about 5 mils thick (about 125micrometers). The TBC layers were deposited using plasma sprayparameters previously described for the inner and outer TBC layers 16and 18 of this invention. As evident from FIG. 4, the first specimensdid not achieve the minimum life requirement identified for the test,whereas the second specimens far exceeded the minimum life requirement.In particular, the specimens with a thickness ratio of less than one(about 0.5) exhibited furnace cycle lives of greater than five timesgreater than the specimens with a thickness ratio of greater than one(about 4).

From these tests, it was shown that, in addition to the compositionaland porosity differences between the inner and outer TBC layers 16 and18, it is important that their thickness ratio (outer/inner) is notgreater than one. From these tests, it was further concluded thatpreferred thickness ratios are less than one, with ratios of not greaterthan 0.5 believed to be particularly preferred. The individualthicknesses of the TBC layers 16 and 18 can be varied to achieve thedesired ratio. For example, the inner TBC layer 16 may have a thicknessof 50 micrometers up to about 500, for example, a nominal thickness ofabout 250 micrometers, and the outer TBC layer 18 may have a thicknessof 25 micrometers up to about 250, for example, a nominal thickness ofabout 125 micrometers.

The preference for limiting the yttria content of the outer TBC layer 18was further established through cyclic thermal gradient tests performedat about 2600° F. (about 1425° C.) with specimens coated with an innerlayer of 7% YSZ and an outer layer of either 38% YSZ or 55% YSZ. Eachlayer was deposited by thermal spraying using the appropriate depositionparameters previously described for the inner and outer TBC layers 16and 18 of this invention, and to have a thickness and porosity withinthe corresponding ranges described above. The specimen with the outerlayer of 55% YSZ spalled at 66 cycles, whereas the specimen with theouter layer of 38% YSZ specimen had not spalled after completing 1983cycles. Consequently, it was concluded that preferred outer TBC layers18 of this invention should contain less than 55 wt. % yttria,particular at surface temperatures of about 2600° F. (about 1425° C.).

From the above, it should be appreciated that the characteristics of theouter TBC layer 18, specifically, a higher yttria content, greaterdensity (less porosity), and lesser thickness relative to the inner TBClayer 16, enable the TBC system 10 to not only mitigate the deleteriouseffects of CMAS deposits, but also exhibit acceptable thermal cyclinglives. As such, the TBC system 10 is particularly well suited forprotecting hot section components of gas turbine engines, and is capableof enabling such components to operate for longer durations and/or athigher temperatures.

While the invention has been described in terms of specific embodiments,it is apparent that other forms could be adopted by one skilled in theart. Therefore, the scope of the invention is to be limited only by thefollowing claims.

1. A process of forming a coating system on a component, the processcomprising: depositing a bond coat on a surface of the component;depositing an inner ceramic layer on the bond coat using a thermal sprayprocess to yield a microstructure characterized by splats and horizontalporosity, the inner ceramic layer consisting essentially of zirconiastabilized by about 6 to about 9 weight percent yttria and beingdeposited to have a thickness and a porosity level; depositing an outerceramic layer on the inner ceramic layer using a thermal spray processto yield a microstructure characterized by splats and horizontalporosity, the outer ceramic layer defining an outermost surface of thecoating system and consisting essentially of zirconia stabilized byabout 25 to about 75 weight percent yttria, the outer ceramic layerbeing deposited to have a porosity level that is higher than the innerceramic layer and to have a thickness that is less than the thickness ofthe inner ceramic layer such that a ratio of the thickness of the outerceramic layer to that of the inner ceramic layer is less than 1.0; andthen heat treating the inner and outer ceramic layers in a vacuum to atemperature and for a duration sufficient to relieve stresses thereininduced by the depositing steps.
 2. The process according to claim 1,wherein the heat treating step is performed at a temperature of about1050 to about 1080° C. in a vacuum for a duration of about two to aboutfour hours.
 3. The process according to claim 1, wherein the ratio ofthe thickness of the outer ceramic layer to that of the inner ceramiclayer is not greater than 0.5.
 4. The process according to claim 1,wherein the porosity level of the outer ceramic layer throughout thethickness thereof is less than that of the inner ceramic layer.
 5. Theprocess according to claim 4, wherein the outer and inner ceramic layersare deposited so that the porosity level of the inner ceramic layer isabout 10 to about 25 volume percent
 6. The process according to claim 4,wherein the outer and inner ceramic layers are deposited so that theporosity level of the outer ceramic layer is about 3 to about 15 volumepercent.
 7. The process according to claim 1, wherein the outer ceramiclayer is deposited to consist essentially of zirconia stabilized byabout 38 to less than 55 weight percent yttria and the outer and innerceramic layers define a thickness ratio of not greater than 0.5.
 8. Theprocess according to claim 1, wherein the outer ceramic layer isdeposited to consist essentially of a cubic crystal phase and the innerceramic layer is deposited to consist essentially of a tetragonal ormodified tetragonal crystal phase.
 9. The process according to claim 1,wherein the component is a gas turbine engine component and the processfurther comprises reacting the outer ceramic layer with a depositcontaining calcia, magnesia, alumina and silica to form calcium yttriumsilicate.
 10. The process according to claim 1, wherein the innerceramic layer is deposited to have a thickness of at least 50 to about500 micrometers.
 11. The process according to claim 1, wherein the outerceramic layer is deposited to have a thickness of up to 250 micrometers.12. The process according to claim 1, wherein the outer ceramic layer isdeposited to have a thickness of at least about 25 micrometers.
 13. Theprocess according to claim 1, wherein the outer ceramic layer reactswith a eutectic compound containing calcia, magnesia, alumina and silicato form calcium yttrium silicate at temperatures above 1200° C.
 14. Theprocess according to claim 1, wherein the bond coat is a metallic bondcoat chosen from the group consisting of MCrAlX overlay coatings and/ordiffusion aluminide coatings.
 15. The process according to claim 1,wherein the component is a gas turbine engine component formed of anickel-base or cobalt-base superalloy.
 16. The process according toclaim 1, wherein the component is chosen from the group consisting ofhigh and low pressure turbine vanes and blades, shrouds, combustorliners and augmentor hardware of a gas turbine engine.